According to API RP 571, high-cycle fatigue (HCF) is characterized by very tight, narrow cracks that can escape detection using typical NDE methods due to their minimal opening displacement and fine geometry.

From API RP 571 Section 5.2.1 (Fatigue - High Cycle):

"The cracks are usually tight and may be difficult to detect using conventional NDE techniques such as PT or MT. UT and RT may also have difficulty identifying these small, tight flaws, especially in early stages of propagation."

The primary issue in NDE is not the geometry (such as 90° corners) or ID location, but rather the tightness and early-stage subtlety of the cracks which results in reduced detectability. Therefore, option B is correct as it aligns most accurately with API RP 571's detailed characterization of HCF detection challenges.

In steam systems, the absence of a steam trap allows condensate to accumulate, which can lead to corrosion from oxygen and carbon dioxide dissolved in the water—a classic case of condensate corrosion.

From API RP 571 Section 5.3.3.1 (Condensate Corrosion):

“If steam lines or equipment like soot blowers do not have proper drainage or steam traps, condensate may accumulate... Corrosion results from the presence of dissolved oxygen and/or carbon dioxide in the condensate.”

Thus, the correct answer is Option D (condensate corrosion).

API RP 571 under Atmospheric Corrosion notes:

“The highest corrosion rates are typically observed between 80°F and 120°F (27°C–49°C), particularly when relative humidity is high and surfaces are wet from condensation or rain.”

“At higher temperatures, surface dryness generally reduces corrosion activity despite increased reaction kinetics.”

(Reference: API RP 571, Section 4.3.1.3 – Atmospheric Corrosion)

Thus, among the listed temperatures, 175°F is closest to the upper end of the most active corrosion window, making option A the most accurate answer.

According to API RP 571 and API RP 583:

“The most effective mitigation of CUI is the use of appropriate coatings underneath the insulation, which are resistant to moisture and chloride ingress.”

“Inspection and insulation selection are also important but are secondary controls.”

(Reference: API RP 571, Section 4.3.4 – Corrosion Under Insulation; API RP 583)

Hence, option D is correct.